Abstract The present work is to study the production and characterization of biochar produced at two different temperatures (400 and 900 °C) and its influence on the interaction of biochar with elastomers of different polarity, aiming at the replacement of carbon black in elastomer compounds, based on the rheometric, physical, chemical and mechanical properties. The biochar production temperature of 900 ºC affected the optimum vulcanization time (t90), with compounds containing NR and NBR having the shortest vulcanization times because temperatures above 400 ºC produce an alkaline biochar that accelerates vulcanization. The biochar interacted with the two elastomers, being superior to NBR due to the oxygen concentration. Therefore, the blends with biochar showed a demonstrated reinforcement of the tensile strength, even if the biochar had a surface area of 3 m2.g-1 for the observed irregular surface, in addition to the mechanical properties, analogous to the blends with carbon black.

ABSTRACT An asymmetric membrane of polysulfone (PSf) was synthesized by phase inversion method. Permeation experiments were carried out between 2 to 5 bar pressure, and at temperatures 20 to 45°C. The dense-selective layer of PSf membrane presents regular thickness (about 5 µm), and was not possible to observe the formation of macrovoids in porous layer. The CO2 permeability through membrane was 18.8 Barrer at 35°C and 2 bar pressure, and this relationship between the pressure and the CO2 permeability was described adequately by Dual-mode model. The absence of CH4 permeability at 2 and 3 bar pressure, qualifies the PSf membrane for gases separation with high selectivity in this range.